期刊
GREEN CHEMISTRY
卷 11, 期 11, 页码 1808-1814出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/b915746h
关键词
-
资金
- West Virginia University's Wood Utilization Project
- Department of Social Justice
Endoglucanase was used to hydrolyze recycled pulp to produce cellulose nanocrystals. The highest yields of cellulose nanocrystals were obtained by treatment with 84 EGU of endoglucanase per 200 mg recycled pulp at 50 degrees C for 60 min of microwave and conventional heating. Of the two modes of heating investigated, microwave heating at each treatment gave a higher yield than conventional heating. Transmission and scanning electron microscopic analysis of suspensions showed cellulose nanocrystals with widths of 30 nm to 80 nm and lengths of 100 nm to 1.8 mu m). This was within range of the length of cellulose crystals (100 nm to 3.5 mu m) obtained using dynamic light scattering analysis. The average zeta potential of cellulose nanocrystals was -31.37 mV. X-ray diffraction of cellulose nanocrystals, recycled pulp and residues of recycled pulp shows a gradual change in the particle size.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据