Cellulose was dissolved rapidly in 7 wt% NaOH/12 wt% urea aqueous solution pre-cooled to -12 degrees C within 2 min to obtain its solution, which is a green process. A series of regenerated cellulose (RC) films were prepared from the cellulose solution via a simple and low-cost method to evaluate their structure and properties as packaging and functional materials. The cellulose films were treated successfully with fluorescent dyes and photoluminescent (PL) pigments to fabricate, for the first time, novel PL materials, which exhibited strong fluorescence and long after-glow emission. The results from CP/MAS C-13 NMR spectra, X-ray diffraction and tensile testing confirmed that the transparent RC films possessed an homogenous structure, excellent optical transmittance (90% at 800 nm), as well as good tensile strength. Moreover, the drawing process could significantly improve their tensile strength, which reached 138 MPa. In addition, the biodegradation tests revealed that the RC films could be biodegraded completely. This work provided a non-toxic solvent system for the preparation of the packaging films and PL materials. This process is promising on a large scale and will maintain clean air in the production environment.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据