JOURNAL OF WUHAN UNIVERSITY OF TECHNOLOGY-MATERIALS SCIENCE EDITION
卷 30, 期 6, 页码 1198-1203出版社
WUHAN UNIV TECHNOLOGY
DOI: 10.1007/s11595-015-1295-2
关键词
explosive welding; interface; TEM; intermetallic compound; fracture
资金
- National Natural Science Foundation of China [U1332110, 50971038]
- Project of Liaoning BaiQianWan Talents Program of China [2013921071]
It was aim to investigate the interfacial microstructure and shear performance of Ti/Cu clad sheet produced by explosive welding and annealing. The experimental results demonstrate that the alternate distribution of interfacial collision and vortex of flyer layer forms in the interface a few of solidification structure. TEM confirms that the interfacial interlayer contains obvious lattice distortion structure and intermetallic compounds. It interprets the explosive welding as the interfacial deformation and thermal diffusion process between dissimilar metals. The interfacial shear strength is very close to the Cu matrix strength, which is determined by the mixture of the mechanical bonding and metallurgical bonding. Several cracks exist on the shear fracture owing to the intermetallic compound in the interfacial solidification structure and also the probable welding inclusion.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据