期刊
FUNCTIONAL MATERIALS LETTERS
卷 4, 期 2, 页码 171-174出版社
WORLD SCIENTIFIC PUBL CO PTE LTD
DOI: 10.1142/S179360471100183X
关键词
Chlorine gas sensor; solid electrolyte
资金
- European Union [POIG.01.03.01-02-002/08-00]
La1-xMgxOCl1-x (x = 0.025, 0.05 and 0.1) and La0.9Ca0.1OCl0.9 samples were prepared by a solid state reaction method. The best preparation conditions were determined by means of the differential thermal analysis and thermogravimetry (DTA&TG). The samples were studied by X-ray diffraction (XRD) analysis. Electrical conductivity of La0.9Mg0.1OCl0.1 was measured using electrical impedance spectroscopy (EIS). The prototype chlorine gas sensor was constructed from La0.9Mg0.1OCl0.1 solid electrolyte. The source voltage (SV) of the constructed device was measured as a function of temperature (500-800 degrees C), Cl-2 gradient partial pressure and time. Similar measurements of SV was carried out in atmosphere of synthetic air in argon.