期刊
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
卷 120, 期 2, 页码 1327-1335出版社
SPRINGER
DOI: 10.1007/s10973-015-4425-3
关键词
Microencapsulation; Ammonium polyphosphate; Flame retardancy; Polyurethane foam
资金
- National Natural Science Foundation of China [51003123, 51303004]
- Zhujiang Science & Technology New-star Program of Guangzhou, China [2013J2200016]
- Integration of Industry, Education and Research of Guangdong Province Project [2011A091000007]
Microencapsulated ammonium polyphosphate MFAPP or VMFAPP with shell of melamine-formaldehyde or poly (vinyl alcohol)-melamine-formaldehyde resin was prepared by in situ polymerization, respectively. The flame-retardant performance of rigid polyurethane foam (PU) containing MFAPP or VMFAPP was analyzed by limiting oxygen index and UL-94 test. Thermal degradation behaviors of PUAPP, PUMFAPP and PUVMFAPP were studied using TG and TG-FTIR. Above results indicated that VMFAPP and MFAPP have better water resistance and flame retardancy compared with ammonium polyphosphate (APP) in PU composites. Flame-retardant properties of PUMFAPP and PUVMFAPP composites were rarely changed after hot water treatment. Due to better compatibility and the presence of active groups on the surface of APP, microencapsulation demonstrated a positive effect on the mechanical property of PU composites.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据