期刊
JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
卷 121, 期 2, 页码 619-626出版社
SPRINGER
DOI: 10.1007/s10973-015-4598-9
关键词
Flame retardancy; Ethylene vinyl acetate (EVA); Synergistic effect; Halogen free
资金
- European Commission
- European Project COST Action [MP1105]
- Ramon y Cajal Grant [RYC-2012-10737]
Flame-retardant ethylene vinyl acetate (EVA) composite based on aluminum trihydroxide (ATH), layered double hydroxide (LDH) and organo-modified zirconium phosphate (mZrP) were prepared by melt-compounding method. The synergistic effect of LDH and mZrP with ATH on the fire behavior and thermal stability of EVA composites was studied by limiting oxygen index, UL-94 test, cone calorimeter and thermogravimetric analysis. EVA composite with ATH and LDH passed the V-0 rating while EVA composite with ATH and mZrP exhibited relatively low peak heat release rate. EVA/ATH composite with 10 mass% LDH exhibited a char yield of 34 % at 700 degrees C, while its counterpart with 10 mass% mZrP showed 29 %, indicating LDH possessed superior flame-retardant synergistic efficiency with ATH over mZrP in terms of promoting char formation. Regarding the heat release rate (HRR), EVA/ATH composite with 10 mass% mZrP displayed a 73 % reduction in PHRR, whereas its counterpart with the equivalent loading of LDH showed a lower flame-retardant synergistic efficiency (a 58 % reduction in peak HRR). The results above demonstrated that LDH mainly functioned as catalyst in char formation, while mZrP was beneficial to restraining heat release.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据