Gas sensor; Conductive polymers; Nano-stracture; Polypyrrole; Chemical vapor deposition; Volatile organic compounds; Interdigital electrodes
资金
- Tarbiat Modares University Research Council
- Iran National Science Foundation (INSF)
In this work, the electrical conductive polymer is formed by vapor phase polymerization of pyrrole on the copper interdigital electrodes (Cu-IDEs) in the presence of Fe(III) as an oxidant at room temperature under atmospheric condition. Electrical resistance of IDEs covered with polypyrrole (PPy) layer was investigated and the relationship between the normalized electrical resistances (R - R (0)/R (0)), experimental conditions of vapor-phase coating (amount of oxidant and time coating) and response behavior of sensors to the volatile organic compounds were studied. The results showed that the pattern of response and selectivity of the sensor is affected by vapor phase polymerization conditions. The prepared PPy gas sensors were used at different conditions for detection and measurement of volatile organic compounds in the gas phase. The PPy gas sensors had demonstrated fast response time (< 1 s). Morphological study of the PPy coated layer by scanning electron microscope (SEM) showed that the conducting polymer prepared with nanotube shape. One of the sensors showed selective response toward of n-butylamine (PPy7) with the detection limit of 1 A mu g and linear range of 2-74 A mu g. The PPy7 gas sensor was used to measure n-butylamine in well water sample. Disperse liquid-liquid microextraction (DLLME) method was used for extraction and pre-concentration of n-butylamine from aqueous solutions. The extraction recovery of the proposed method was founded 93-105 %.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据