FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
卷 34, 期 8, 页码 581-591出版社
WILEY-BLACKWELL
DOI: 10.1111/j.1460-2695.2010.01549.x
关键词
crack growth; dissimilar weld; fatigue strength; fracture mechanism; friction stir spot welding
A6061 and low carbon steel sheets, whose thicknesses were 2 mm, were welded by a friction stir spot welding (FSSW) technique using a scroll grooved tool without probe (scroll tool). Tensile-shear fatigue tests were performed using lap-shear specimens at a stress ratio R = 0.1, and the fatigue behaviour of dissimilar welds was discussed. Tensile-shear force of the dissimilar welds was higher than that of the A6061 similar ones. Furthermore, the dissimilar welds exhibited nearly the same fatigue strengths as the A6061 similar ones, indicating FSSW by a scroll tool was effective technique for joining aluminium to steel sheet. Fatigue fracture modes of the dissimilar welds were dependent on load levels, where shear fracture through the interface between A6061 and steel occurred at high load levels, while crack grew through A6061 sheet at low load level.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据