FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
卷 31, 期 9, 页码 812-821出版社
WILEY
DOI: 10.1111/j.1460-2695.2008.01267.x
关键词
fatigue; fracture mode; tension; texture; twinning
资金
- European Union [AST4-CT-2005516152]
- Greek Secretariat of Research and Technology
The mechanical behaviour of two hot rolled magnesium alloys, namely the AZ31 and AZ61, has been evaluated experimentally under both monotonic and cyclic loading. Both longitudinal (L) and long transverse (LT) directions were evaluated. The tensile behaviour of the L and LT directions is similar and differs only in the offset 0.2% yield strength for both materials. This difference is attributed to the angular spread of basal poles toward the rolling direction and is more pronounced for the case of AZ31. A distinct hardening response is obvious in both directions. Twinning formation was observed; it is more pronounced in the longitudinal direction while the fracture mode is intergranular and equiaxed facets are present in the fracture surfaces of the specimens. The S-N curves exhibit a smooth transition from the low to high cycle fatigue regime. AZ61 exhibits an overall better fatigue behaviour compared to AZ31. A transgranular crack initiation mode is observed in all tested specimens while the propagation of the cracks is characterized as intergranular.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据