JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 35, 期 8, 页码 2391-2401出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2015.02.004
关键词
Spray drying method; Transparent ceramics; YAG; Forming performance
资金
- Priority Academic Program Development of Jiangsu Higher Education Institutions (PAPD)
- National Natural Science Foundation of China [51402133, 51302115, 61405081]
Spray drying parameters have been systematically optimized to granulate a stoichiometric mixture of commercial oxides for YAG transparent ceramics. The processing parameters and suspension composition were changed in sequence and SEM analysis, EDS, MIP and transmittance measurements, were used to choose the best spray drying parameters. The optimized inlet and outlet temperatures of drying medium were 75 and 60 degrees C, and its flux and aspiration rate were 25 Hz and 30 Hz, respectively. The balanced suspension composition were: solid content 45 wt.%, binder PVB 1.0 wt.%, dispersant DS005 0.50 wt.% and the atomizer rotating speed 8000 r/min. The granulated particles exhibited excellent forming performance with mono-dispersed, spherical and fully dense aggregates, and mean size was similar to 40 mu m. They could be crushed under 40 MPa. The homogeneous distribution and microstructure of ceramics assured the high optical quality of YAG ceramics. (C) 2015 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据