EXPRESS POLYMER LETTERS
卷 6, 期 10, 页码 794-804出版社
BUDAPEST UNIV TECHNOL & ECON
DOI: 10.3144/expresspolymlett.2012.85
关键词
nanocomposites; isolation techniques; cellulose; reinforcements
资金
- Major State Basic Research Development Program of China [2010CB732206]
- Doctoral Program Foundation of Institutions of Higher Education of China [20090172110022]
Three techniques including acid hydrolysis (AH), 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO)-mediated oxidation (TMO) and ultrasonication (US) were introduced to isolate nanocellulose from microcrystalline cellulose, in order to reinforce poly(vinyl alcohol) (PVA) films. Important differences were noticed in fiber quality of nanocellulose and film properties of PVA nanocomposite films. The TMO treatment was more efficient in nanocellulose isolation with higher aspect ratio, surface charge (-47 mV) and yields (37%). While AH treatment resulted in higher crystallinity index (88.1%) and better size dispersion. The fracture surface, thermal behavior and mechanical properties of the PVA nanocomposite films were investigated by means of scanning electron microscopy (SEM), differential scanning calorimetry (DSC), thermogravimetric analysis (TGA) and tensile testing. The results showed that both the TMO-derived and AH-derived nanocellulose could be dispersed homogeneously in the PVA matrices. AH/PVA films had higher elongation at break (51.59% at 6 wt% nanocellulose loading) as compared with TMO/PVA, while TMO/PVA films shown superior tensile modulus and strength with increments of 21.5% and 10.2% at 6wt% nanocellulose loading. The thermal behavior of the PVA nanocomposite films was higher improved with TMO-derived nanofibrils addition.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据