JOURNAL OF THE ELECTROCHEMICAL SOCIETY
卷 162, 期 12, 页码 C638-C647出版社
ELECTROCHEMICAL SOC INC
DOI: 10.1149/2.0131512jes
关键词
-
资金
- Elements Strategy Initiative for Structural Materials (ESISM) through the Ministry of Education, Culture, Sports, Science and Technology (MEXT) of Japan
- Japan Society for the Promotion of Science for Young Scientists
The hydrogen distribution in a hydrogen-charged Fe-18Mn-1.2C (wt%) twinning-induced plasticity austenitic steel was studied by Scanning Kelvin Probe Force Microscopy (SKPFM). We observed that 1-2 days after the hydrogen-charging, hydrogen showed a higher activity at twin boundaries than inside the matrix. This result indicates that hydrogen at the twin boundaries is diffusible at room temperature, although the twin boundaries act as deeper trap sites compared to typical diffusible hydrogen trap sites such as dislocations. After about 2 weeks the hydrogen activity in the twin boundaries dropped and was indistinguishable from that in the matrix. These SKPFM results were supported by thermal desorption spectrometry and scanning electron microscopic observations of deformation-induced surface cracking parallel to deformation twin boundaries. With this joint approach, two main challenges in the field of hydrogen embrittlement research can be overcome, namely, the detection of hydrogen with high local and chemical sensitivity and the microstructure-dependent and spatially resolved observation of the kinetics of hydrogen desorption. (C) 2015 The Electrochemical Society. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据