期刊
EUROPEAN POLYMER JOURNAL
卷 44, 期 5, 页码 1346-1357出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.eurpolymj.2008.02.014
关键词
nanocomposites; blown films; HDPE; rheological properties; transport properties
In this work, high density polyethylene (HDPE) was mixed in a twin screw extruder with organophilic treated clay, Cloisite 20A, and a compatibility agent, a HDPE grafted with maleic anhydride (PEMA). The screw profile was changed from a less dispersive (Profile 1) to a high dispersive configuration (Profile 2). A masterbatch procedure was used to obtain a final organoclay concentration of 5 wt.%. Both profiles allowed the intercalation of the HDPE into the clay, increasing the clay's gallery distance to 3.7 nm. However, the samples produced with Profile 2 (Nano 2 samples) were more elastic and had a more stable structure than the samples produced with Profile 1. Therefore, two kind of blown films of Nano 2 samples were made: FN1 and FN2. The last one was blown at a higher screw velocity than the FN1. Both films had an increase of 95% in the elastic modulus and a reduction of 60% and 45% in O-2 and water vapor permeability rates, respectively, compared to the film of pure HDPE. However, the FN2 structure was more unstable than the FN1 structure. It was concluded that both screw profiles gave the same level of HDPE intercalation in the clay; however, the more dispersive profile produced more time-stable and elastic structures. The increase in the elongation rate during the film blowing process produced also more time-stable morphologies; however, this higher orientation created matrix/filler interfacial defects. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据