The purpose of this study was to evaluate and compare the force levels of aesthetic Ni-Ti wires to regular Ni-Ti wires of the same dimension and evaluate their mechanical properties. Aesthetic and regular maxillary superelastic Ni-Ti wires (0.016 x 0.022) from four different manufacturers (G&H Wire Company, TP Orthodontics, GAC International, and Ortho Organizers) were selected and grouped I-IV. The loading and unloading values were compared using a three-point bending test. The unloading end values were also recorded to evaluate the recovery of archwires after each deflection. The unloading values were recorded at 0.5, 1.5, and 2.5 mm after loading deflections of 1, 2, and 3 mm, respectively. Cross-sectional scanning electron microscopy was used to assess the coating thickness of aesthetic wires. The results, statistically analysed, showed a significant decrease in force values for the aesthetic wires in groups I, III, and IV (P < 0.001) as compared to regular Ni-Ti wires of the same dimension from the same manufacturer. There was no significant difference in force values for group II wires. A statistically significant decrease in force values of epoxy-coated wires was observed in groups I, III, and IV only. This is of obvious clinical significance during wire selection. The group II coated wires, however, exhibited forces comparable to their regular Ni-ti wires with a difference that was statistically insignificant. The end values of aesthetic wires showed almost complete recovery for groups I, II, and III after 2 and 3 mm deflections.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据