期刊
EUROPEAN JOURNAL OF INORGANIC CHEMISTRY
卷 -, 期 30, 页码 4691-4699出版社
WILEY-V C H VERLAG GMBH
DOI: 10.1002/ejic.201100381
关键词
Complex metal oxides; Magnetic properties; Multiferroics; Neutron diffraction; Structure elucidation
资金
- Royal Swedish Academy of Sciences
- Swedish Research Council (VR)
- Goran Gustafsson Foundation
- Russian Foundation for Basic Research
The complex metal oxides Mn(2)ASbO(6) (A = In, Sc) with a corundum-related structure A(3)BO(6) were prepared as polycrystalline powders by a solid-state reaction route. Their crystal structure and magnetic properties were investigated by using a combination of X-ray and neutron powder diffraction, electron microscopy, calorimetric, and magnetic measurements. At room temperature, these compounds adopt a trigonal structure, space group R (3) over bar, with a = 8.9313(1) angstrom, c = 10.7071(2) angstrom (for In) and a = 8.8836(1) angstrom, c = 10.6168(2) angstrom (for Sc), which persists down to 1.6 K. The Mn and A cations were found to be randomly distributed over the A sites. The overall behavior of the magnetization of Mn2InSbO6 and that of Mn2ScSbO6 are quite similar. In spite of the relatively large amount of Mn ions on the A site, only short-range magnetism is observed. Neutron diffraction patterns of Mn2InSbO6 showed no evidence of a long-range magnetic ordering at 1.6 K, instead only a weak diffuse magnetic peak was observed at low temperatures. The factors governing the observed structural and magnetic properties of Mn(2)ASbO(6) are discussed and compared with those of other Mn-containing complex metal oxides with a corundum-related structure. The influence of the A cation sublattice on the magnetic properties is also considered.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据