Aggregation and surface properties of iron oxide nanoparticles: Influence of pH and natural organic matter

The interactions between unpurified manufactured nanoparticles (NPs; iron oxide NPs, similar to 7 nm) and standard Suwannee River humic acid (SRHA) were investigated under a range of environmentally relevant conditions. At low pH, approximately 35% of the total iron was in the dissolved phase (< 1 kDa), present from the initial synthesis, whereas at pH more than 4, this concentration was negligible because of the formation of new particles via hydrolysis. Dynamic light scattering results indicated that extensive aggregation of NPs began at approximately pH 5 to 6 and reached a maximum at approximately pH 8.5, whereas with added SRHA, aggregation was shifted to lower pH values of 4 to 5 and was affected by SRHA concentration. Aggregation could be explained mainly by charge neutralization. Further, more detailed investigations by flow field-flow fractionation and transmission-electron microscopy were performed under a more restricted set of conditions (pH 2 - 6) to examine the aggregation process. Results indicated the formation of SRHA surface coating on iron oxide NPs of approximately 1 nm and the increase in thickness of this coating with the increase of SRHA concentration. Iron oxide NPs were shown to form increasingly large aggregates with increases in both pH (from 2 to 6) and SRHA concentration (from 0 to 25 mg/L). The structure and aggregation mechanism of these aggregates were found to be both pH and SRHA concentration dependent, with open, porous aggregates in the absence of SRHA and compact aggregates in the presence of SRHA.