期刊
ENVIRONMENTAL TECHNOLOGY
卷 33, 期 16, 页码 1927-1936出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/09593330.2011.651162
关键词
maghemite; nanoparticle; arsenate; adsorption; desorption; regeneration
资金
- Maa-ja vesitekniikan tuki ry
Maghemite (gamma-Fe2O3) nanoparticles are potential adsorbents for arsenate removal from drinking water. Arsenate, As(V) oxoanion, removal is crucial due to arsenate's serious effects on health and its existence in water worldwide. The aim of the present study was to investigate the adsorbent properties of maghemite nanoparticles by observing their stability, desorption and regeneration ability. Arsenate batch desorption and regeneration experiments were carried out with two different kinds of maghemite - a commercial product and a laboratory-synthesized one using the sol-gel process. The best alkaline desorption solution was determined from five different alkaline solutions: NaOH, Na2CO3, Na2HPO4, NaHCO3 and CH3COONa center dot 3H(2)O (NaAc). Desorption kinetics were also examined. NaOH was observed to be the best desorption solution at a concentration of 1M with >95% desorption efficiency achieved for both adsorbents. The arsenate adsorption-desorption process was reversible and maghemite recovery was efficient at successive cycles. The laboratory-synthesized maghemite maintained more than 95% of its initial uptake capacity after six cycles for initial As(V) concentrations of 500 and 1000 mu g/l, while the achievement with the commercial product was two to four cycles. In addition, iron dissolution from adsorbents was negligible. Thus, it is possible to regenerate the maghemite nanoparticles for repeated adsorption of As(V).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据