Performance evaluation of a continuous flow photocatalytic reactor for wastewater treatment

A novel photocatalytic reactor for wastewater treatment was designed and constructed. The main part of the reactor was an aluminum tube in which 12 stainless steel circular baffles and four quartz tube were placed inside of the reactor like shell and tube heat exchangers. Four UV-C lamps were housed within the space of the quartz tubes. Surface of the baffles was coated with TiO2. A simple method was employed for TiO2 immobilization, while the characterization of the supported photocatalyst was based on the results obtained through performing some common analytical methods such as X-ray diffraction (XRD), scanning electron microscope (SEM), and BET. Phenol was selected as a model pollutant. A solution of a known initial concentration (20, 60, and 100 ppmv) was introduced to the reactor. The reactor also has a recycle flow to make turbulent flow inside of the reactor. The selected recycle flow rate was 7x10(-5) m(3).s(-1), while the flow rate of feed was 2.53x10(-7), 7.56x10(-7), and 1.26x 10(-6) m(3).s(-1), respectively. To evaluate performance of the reactor, response surface methodology was employed. A four-factor three-level Box-Behnken design was developed to evaluate the reactor performance for degradation of phenol. Effects of phenol inlet concentration (20-100 ppmv), pH (3-9), liquid flow rate (2.53x10(-7)-1.26x10(-6) m(3).s(-1)), and TiO2 loading (8.8-17.6 g.m(-2)) were analyzed with this method. The adjusted R-2 value (0.9936) was in close agreement with that of corresponding R-2 value (0.9961). The maximum predicted degradation of phenol was 75.50% at the optimum processing conditions (initial phenol concentration of 20 ppmv, pH similar to 6.41, and flow rate of 2.53x10(-7) m(3).s(-1) and catalyst loading of 17.6 g.m(-2)). Experimental degradation of phenol determined at the optimum conditions was 73.7 %. XRD patterns and SEM images at the optimum conditions revealed that crystal size is approximately 25 nm and TiO2 nanoparticles with visible agglomerates distribute densely and uniformly over the surface of stainless steel substrate. BET specific surface area of immobilized TiO2 was 47.2 and 45.8 m(2) g(-1) before and after the experiments, respectively. Reduction in TOC content, after steady state condition, showed that maximum phenol decomposition occurred at neutral condition (pH similar to 6).