Corrosion fatigue; Biaxial fatigue; Mixed mode; Crack growth rate; Aluminum alloys
类别
资金
- Office of Corrosion Policy and Oversight, OSD, Washington, DC
Biaxial and uniaxial fatigue crack growth of aluminum alloy 7075-T6 was characterized under air and salt water (3.5%) environments. Biaxial fatigue increased crack growth rate in region I relative to uniaxial fatigue under both environments. Biaxial fatigue increased crack growth rate in region 11 relative to uniaxial fatigue under salt environment. Crack growth rates in region I were comparable in air and salt environments, while they were faster in salt water than air environment in region II. Biaxial fatigue in salt environment exhibited intergranular cracks along with main transgranular fracture. A mechanism for biaxial corrosion fatigue crack growth is proposed. Published by Elsevier Ltd.