Martensitic stainless steel; Hydrogen embrittlement; Retained austenite; Phase transformation
Retained austenite may play a role in the hydrogen embrittlement process because austenite has much higher hydrogen solubility than martensite has. The effect of the retained austenite on hydrogen cracking was investigated by tensile testing of standard round bar specimens that had been heat treated in order to achieve different levels of retained austenite. A significant effect of the retained austenite was observed. Samples with high amounts of retained austenite experienced a much higher reduction in ductility after hydrogen charging than samples with low amounts of retained austenite. In order to explain this effect, the hydrogen solubility of samples containing different levels of austenite and precipitates was measured. This was achieved by charging the samples to saturation in an electrolyte and performing hydrogen analysis. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据