期刊
ENGINEERING FAILURE ANALYSIS
卷 19, 期 -, 页码 22-31出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.engfailanal.2011.09.003
关键词
Creep rupture; Failure analysis; Void; Welds; Microanalysis
资金
- National Natural Science Foundation of China [50975196, 50805103]
- Tianjin Nature Science Foundation of China [08JCZDJC18100, 08JCYBJC09100]
- Research Fund for the Doctoral Program of Higher Education of China [20090032110026]
The microstructure degradation and creep damage evolution process of Type IV cracking in a 9Cr-0.5Mo-1.8 W-VNb steel (ASME P92) welded joint during creep were investigated. Creep tests were carried out at 923 K and 70 MPa, and terminated at specific times in order to analyze the microstructure change and the creep voids formation in the welded joint. The welded joint finally ruptured in the fine grained heat affected zone adjacent to the base metal, identified as Type IV cracking. It revealed that the creep strength in the fine grained heat affected zone was lower than other zones of the welded joint. Creep voids were likely to nucleate and grow in this zone. In addition, carbides played an important role as nucleating sites for creep voids. As the creep time increased, creep voids linked to each other and finally formed micro-cracks resulting in the fracture in the fine grained heat affected zone. On the basis of microstructure degradation and creep voids propagation, the creep damage evolution process was proposed. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据