Lithium plating in a commercial lithium-ion battery A low-temperature aging study

期刊

JOURNAL OF POWER SOURCES
卷 275, 期 -, 页码 799-807

出版社

ELSEVIER SCIENCE BV
DOI: 10.1016/j.jpowsour.2014.11.065

关键词

Lithium plating; Low-temperature aging; Nondestructive characterization; Cyclable lithium; Cell opening

资金

  1. Helmholtz-Institut Ulm (HIU)
  2. Zentrum fur Sonnenenergie-und Wasserstoff-Forschung Baden-Wfirttemberg (ZSW)

向作者/读者索取更多资源

The formation of metallic lithium on the negative graphite electrode in a lithium-ion (Li-ion) battery, also known as lithium plating, leads to severe performance degradation and may also affect the cell safety. This study is focused on the nondestructive characterization of the aging behavior during long-term cycling at plating conditions, i.e. low temperature and high charge rate. A commercial graphite/LiFePO4 Li-ion battery is investigated in order to elucidate the aging effects of lithium plating for real-world purposes. It is shown that lithium plating can be observed as a loss of cyclable lithium which affects the capacity balance of the electrodes. In this way, lithium plating counteracts its own occurrence during prolonged cycling. The capacity losses due to lithium plating are therefore decreasing at higher cycle numbers and the capacity retention curve exhibits an inflection point. It is further shown that the observed capacity fade is partly reversible. Electrochemical impedance spectroscopy (EIS) reveals a significant increase of the ohmic cell resistance due to electrolyte consumption during surface film formation on the plated lithium. Additional cell opening provides important quantitative information regarding the thickness of the lithium layer and the corresponding mass of the plated lithium. (C) 2014 Elsevier B.V. All rights

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据