JOURNAL OF POWER SOURCES
卷 283, 期 -, 页码 397-407出版社
ELSEVIER SCIENCE BV
DOI: 10.1016/j.jpowsour.2015.02.080
关键词
TiO2 nanotubes; Multi-walled carbon nanotubes; Electrochemical supercapacitor; Silane coupling agent
资金
- National Natural Science Foundation of China [51172159]
A new two-step method is successfully developed for the synthesis of MWNT5-TiO2 nanotube hybrid electrodes. The resulting (3-aminopropyl)triethoxysilane (APS) film was chemisorbed on the surface of TiO2 nanotubes. TiO2 nanotubes surface modified by 5, 10, and 20 mg ml(-1) APS ethanol solution can determine the morphology of MWNTs-TiO2 nanotube electrodes. The morphology and surface composition were characterized by scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), and X-ray photoelectron spectroscopy (XPS) techniques. The zeta potential results confirm that MWNTs were deposited on APS-TiO2 nanotubes by the electrical attractive force. The electrochemical performances were evaluated by using cyclic voltammetry, electrochemical impedance spectroscopy, and galvanostatic charge discharge measurements. The MWNT5-TiO2 nanotube hybrid electrodes (5, 10, and 20 mg ml(-1) APS) exhibited a high specific capacitance of 3.5, 4.4, and 3.4 mF cm(-2) in 1 M H2SO4 aqueous solution at a charge discharge current density of 0.1 mA cm(-2), respectively. Cyclic voltammetric studies indicated that the electrode has excellent stability even after 1000 consecutive CV cycles. Moreover, the galvanostatic charge discharge experiments conducted on the MWNTs-TiO2 nanotube hybrid electrodes (10 mg ml(-1) APS) exhibited long-term cycle stability, retaining about 75% specific capacitance after 1000 cycles, which suggests that it has potential as an electrode material for high-performance electrochemical supercapacitors. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据