Lithium ion battery; Lithium-rich layer-structured cathode material; Open circuit potential; Hysteresis; Oxidation state; Crystal structure
资金
- New Energy and Industrial Technology Development Organization (NEDO) of Japan
There is large hysteresis between charge and discharge curves in lithium-rich layer-structured cathode material, Li1.2Ni0.13Mn0.54Co0.13O2. The mechanism for hysteresis was examined by X-ray diffraction (XRD) and X-ray absorption fine structure (XAFS) measurement as a first step in solving this issue. XRD measurements clarified that there was hysteresis in the lattice parameter between charge and discharge processes. XAFS spectra indicated that transition metals were oxidized and reduced in the same potential region during charge and discharge processes. Oxygen was oxidized at higher potential than transition metals during charge process; however, the former was reduced at lower potential than the latter during discharge process. Therefore, large hysteresis of potential between charge and discharge processes in Li1.2Ni0.13Mn0.54Co0.13O2 was mainly related to the reaction which is compensated with redox of oxygen. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据