Lithium ion battery; Cathode materials; Layered cathode; Excess lithium compound; OCP hysteresis
The layered complex cathode has attracted much interest recently due to its high capacity, which exceeds 250 mAhg(-1). On the other hand, it also shows large voltage hysteresis which causes energy loss when applied as a practical battery material. It has been reported that the hysteresis is an intrinsic bulk property, and the phenomenological model due to the migration of transition metal has been also proposed. Then, it is considered that to study the hysteresis for various compositions of transition metal is valuable to clarify the phenomenon. In this work, the layered complex cathode of 0.5Li(2)MnO(3)-0.5LiNi(1/3)Co(1/3)Mn(1/3)O(2) was investigated. The results are discussed in comparison with the previous reports for 0.5Li(2)MnO(3-)0.5LiMn(0.5)Ni(0.5)O(2). Investigating dOldV profilesrevealed that redox peaks at around 3.75 V showed small dependency on composition of transition metal, while it seemed that a reduction peak at 3.26 V was independent on the composition. Precise measurement of open circuit potential vs. capacity characteristics demonstrated that the energy dissipation during a cycle was abut 26 kJmol(-1). (C) 2014 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据