期刊
ELECTROCHIMICA ACTA
卷 108, 期 -, 页码 112-117出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2013.06.112
关键词
Silicon; Silicon oxide; Electrodeposition; Photoanode; Photoelectrolysis
资金
- Foundation of Polish Science [MPD Program/2008/01]
- EU European Regional Development Fund
- Polish Ministry of Science and Higher Education [N N204 117039]
- CePT project [POIG.02.02.00-14-024/08-00]
We report a low temperature, an electrochemical way of preparation of a photoanode made of n-type silicon oxide based films, at which surface photoelectrochemical oxygen evolution was observed with no need to deposit of other materials. Conditions of electrosynthesis, under which the electrochemical reduction of silicon chlorides in non aqueous solutions leads to silicone oxide based films are described. The photoactivity of prepared photo-anodes was reproducible and the observed photocurrent sustained for many hours. The most stable photocurrent was observed for films deposited at -2.7 V. Water oxidation was observed while occurring at the onset potentials smaller than 0.2 V comparing to the dark water splitting potential. The highest photocurrent was observed at -0.3 V (thermodynamic value 1.02V vs. Ag wire), which means energy saving corresponding to ca. 1.3 V. The results demonstrate that a low temperature electrodeposition of silicon oxide based films can be an alternative route for fabrication of photoanode for water photosplitting devices. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据