Lithium-ion battery; Electrochemical properties; Anode material; Electrospinning
资金
- Australian Research Council (ARC) [LP0991012]
- Wuhan Planning Project of Science and Technology [201011511520]
- Australian Research Council [LP0991012] Funding Source: Australian Research Council
A nano-MoO3/C composite was synthesized using the electrospinning method. Thermal analysis was used to determine the carbon content in the composite. The MoO3/C composite was characterized by Xray diffraction, and the particle size and shape of the MoO3/C composite were observed by scanning and transmission electron microscopy. The results showed that the MoO3/C composite takes on the morphology of nanofibers, with the diameters of the nanofibers ranging from 50 to 200 nm. The nanofibers are composed of amorphous nano-MoO3 and carbon, with the carbon content in the composite about 42% and the MoO3 content about 58%. The electrochemical properties of the MoO3/C composite were also investigated. The MoO3/C composite nanofiber electrodes exhibited both high reversible capacity and good cycling performance when cycled at room temperature in a 3.0-0.01 V potential (vs Li/Li+) window at current density of 40 mA g(-1). The MoO3/C composite retained a discharge capacity of 710 mAh g(-1) after 100 cycles. When the load current density was increased to 800 mA g(-1), the MoO3/C composite still retained a discharge capacity of 300 mAh g(-1) after 100 cycles. The reasons for the outstanding electrochemical properties of the MoO3/C composite are also discussed. (C) 2013 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据