卷 78, 期 -, 页码 406-411出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2012.06.031
关键词
Graphene; NiO; Anode; Lithium ion batteries
资金
- University of Ulsan, Ulsan, Korea
A graphene/NiO composite was prepared by simple chemical precipitation followed by thermal annealing. The results of XRD, FT-IR, FE-SEM, FE-TEM, and EDS analyses confirmed the presence of NiO nanoparticles with plate structure on the graphene surface. The discharge capacities of graphene, graphene/NiO (37 wt.%), and graphene/NiO (59 wt.%) are about 302, 604, and 856 mAh g(-1) at 5000 mA g(-1) (5 C), respectively. The cells containing 59 wt.% NiO show the best performance, and the graphene nanocomposite materials have high rate properties that are comparable to some of the best results reported in the literature using NiO. This graphene/NiO (37 and 59 wt.%) nanocomposite displays superior LIB performance with large reversible capacity, high Coulombic efficiency, good cyclic performance, and excellent rate capability, highlighting the importance of the anchoring of nanoplate structure NiO on graphene sheets for maximum utilization of electrochemically active graphene/NiO for energy storage applications in high-performance LIB. (C) 2012 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据