Fluoroethylene carbonate; Solid electrolyte interphase (SEI) layer; Mn dissolution; LiMn2O4; Graphite
资金
- Ministry of Education, Science and Technology [R31-2008-000-10055-0]
In order to overcome severe capacity fading of LiMn2O4/graphite Li-ion cells at high temperature at 60 degrees C, nuoroethylene carbonate (FEC) was newly evaluated as an electrolyte additive with 2 wt % FEC addition into the electrolyte (EC/DEC/PC with 1 M LiPF6), the capacity retention at 60 degrees C after 130 cycles was significantly improved by about 20%. To understand the underlying principle on the capacity retention enhancement, the electrochemical properties of the cells including cell performance, impedance behavior as well as the characteristics of the interfacial properties were examined. Based oil these results, it is suggested that the improved capacity retention of LiMn2O4/graphite Li-ion cells with addition of FEC especially at high temperature is mainly originated from the thin and stable SEI layer formed oil the graphite anode surface (C) 2009 Elsevier Ltd. All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据