ELECTROCHIMICA ACTA
卷 55, 期 8, 页码 2978-2982出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2010.01.015
关键词
Lithium ion battery; Li4Ti5O12/C/CNTs composite; Li4Ti5O12/C composite; Conductive network; Rate capability
资金
- Ministry of Science and Technology of the People's Republic of China [2006CB932703]
- Chinese Academy of Science [KJCX2-YW-M01]
A Li4Ti5O12/carbon/carbon nano-tubes (Li4Ti5O12/C/CNTs) composite was synthesized by using a solid-state method. For comparison, a Li4Ti5O12/carbon (Li4Ti5O12/C) composite and a pristine Li4Ti5O12 were also synthesized in the present study. The microstructure and morphology of the prepared samples are characterized by XRD and SEM. Electrochemical properties of the samples are evaluated by using galvanostatic discharge/charge tests and AC impedance spectroscopy. The results reveal that the Li4Ti5O12/C/CNTs composite exhibits the best rate capability and cycling stability among the samples of Li4Ti5O12, Li4Ti5O12/C and Li4Ti5O12/C/CNTs. At the charge-discharge rate of 0.5 C, 5.0 C and 10.0 C, its discharge capacities were 163 mAh/g, 148 mAh/g and 143 mAh/g, respectively. After 100 cycles at 5.0 C, it remained at 146 mAh/g. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据