ELECTROCHIMICA ACTA
卷 55, 期 28, 页码 8888-8893出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2010.08.015
关键词
Nanorod assembled spinel Li1 05Mn1 95O4; Synchrotron powder X-ray diffraction; Rate capability; Central-tunneled morphology; Rechargeable lithium ion batteries
资金
- Korea government
- Ministry of Education Science & Technology (MEST) [20090060053]
Nanorod-assembled spinel Li1 05Mn1 95O4 rods with a central tunnel along the rod-axis were synthesized using highly crystalline beta-MnO2 rods as self-templates The synthesized spinel Li1 05Mn1 95O4 is an assembly of several single crystal-like nanorods with an average diameter and length of 100 and 400 nm respectively which was determined by microstructural Rietveld refinement using the synchrotron powder XRD data Galvanostatic battery testing showed that central-tunneled and nanorod-assembled Li1 05Mn1 95O4 rods have a high charge storage capacity at high current densities in comparison with those of the simnel rods without a tunnel structure and commercial powders Moreover a capacity retention value of 81% was observed at the end of 100 cycles at a current of 250 mAh g(-1) (C) 2010 Elsevier Ltd All rights reserved
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据