ELECTROCHIMICA ACTA
卷 55, 期 17, 页码 4837-4844出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2010.02.035
关键词
Duplex stainless steel; Pitting Corrosion; Potentiostatic pulse technique; Inclusion
资金
- National Nature Science Foundation of China [50871031]
- Shanghai Science and Technology Basic Research Key [09JC1401600]
- Shanghai Leading Academic Discipline Project [B113]
Duplex stainless steel simultaneously comprises various phases, inclusions, precipitates and grain boundaries. It is full of academic and valuable significance for materials designing and processing optimization to ascertain the corrosion resistance of corresponding phases and various microstructures. However, up to date, efficient evaluation technique is still scare mainly due to difficulty in controlling of micropits. In this work, for the first time, optimized potentiostatic pulse technique (PPT) was established and applied to study the rule of initiation of pits of solution annealed and aged DSS in 1.0 mol/L NaCl solution. The results showed that the size of pits can be well-controlled by adjusting the condition of potential pulse. Combined with SEM/EDS system observation, it was found that for solution-annealed specimens, sulphide and oxide mixed inclusions were the preferential pit initiation sites, while for aged specimens, majority pits occurred at inclusions in area impoverished in Cr/Mo, which is vicinal to sigma phase. The phenomena that growing pits is retarded by precipitation rich in Cr/Mo, i.e. sigma phase, was testified and explained. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据