卷 53, 期 12, 页码 4137-4145出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2007.12.054
关键词
Li-ion batteries; positive electrode materials; high voltage spinel oxide
High voltage spinel oxides with composition LiMn2-xMxO4 (M, a transition metal element) have remarkable properties Such as high potential, high energy density and high rate capability. We believe that these positive electrode materials could replace the widespread commercial layered nickel cobalt oxides in some applications. The present assessment highlights electrochemical performance of optimized LiNi0.5Mn1.5O4 and Substituted Counterparts, all having a spinel Structure (cubic close-packed oxygen array) similar to the relative LiMn2O4. To fully emphasize the benefit from high potential spinel oxides, tests have been performed versus lithium metal, Li4Ti5O12 and graphite, using various electrode loadings (0.3-4.5 rnAh cm(-2)) and cycling rates (from C/20 to 60C rate). Steady capacity retention ( 130-140 mA h(-1) for nearly 500 cycles) and flat voltage (4.7 V vs. Li+/Li) have been obtained at C/5 rate at room temperature. Effect of cycling at high temperature has been shown to be less critical than For LiMn2O4. High voltage spincl oxides still sustain 100 mAh g(-1) and over after 400 cycles at 55 degrees C at 1C rate. Rate capability is also excellent, with only 4% loss of capacity when comparing C/8 and 8C rates (thin electrodes). (c) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据