期刊
ELECTROCHIMICA ACTA
卷 53, 期 16, 页码 5220-5225出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.electacta.2008.02.047
关键词
duplex stainless steel; pitting corrosion; critical pitting temperature (CPT); critical repassivation temperature (T-r); polarization
Both the critical pitting temperature (CPT) and critical repassivation temperature (T,) for two kinds of duplex stainless steels (DSS, namely UNS S31803 and UNS S32750) were investigated in 1 mol/L NaCl solution using the cyclic thermammetry method. Potentiodynamic anodic polarization technique was employed to validate the cyclic thermammetry technique. In addition, the site of pitting nucleated preferentially on the DSS had been confirmed by scanning electron microscopy (SEM). The results demonstrated that there exhibits a hysteresis loop in cyclic thermammetry curve, revealing that the propagating pits could repassivate during the cooling half-cycle. The CPT and T-r for UNS S31803 were 59.6 degrees C and 36.5 degrees C, whilst the CPT and T-r for UNS S32750 were 87.5 degrees C and 70.5 degrees C, respectively. Pitting was always observed preferentially in the austenite phase. The results can be partially explained based on the changes in chemical composition of ferrite and austenite phases. Moreover, a semi-quantitative model is proposed to explain the existence of T-r. (C) 2008 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据