Proton exchange composite membrane; Ionic liquid; SPEEK; Proton conductivity; Tensile stress; Fuel cells
资金
- Ministry of Education of China [20090042110002]
- Northeastern University in China [90105001]
A composite membrane was fabricated using a novel approach based on the ionic liquids 1-butyl-3-methylimidazolium chloride or 1-butyl-3-methylimidazolium hexafluorophosphate, sulfonated polyetheretherketone (SPEEK), and phosphoric acid. This proton conducting composite membrane shows promise for operation in high temperature proton exchange membrane fuel cells at working temperatures up to 160 degrees C without humidification. Proton conductivity at a level of 2.0 x 10(-2) S/cm was achieved at 160 degrees C by the composite membrane with a molar ratio of 1:0.6:9 for SPEEK, 1-butyl-3-methylimidazolium (BMIM) cation and phosphoric acid, respectively. The sulfonation degree was 0.643 per polymer repeat unit with over 90% of the sulfate fixed anions forming a salt complex with BMIM cations. The tensile stress at break of the composite membrane was 15.5 MPa at room temperature, and it decreased from 4.1 to 1.9 MPa when the temperature increased from 110 to 160 degrees C, respectively. (c) 2010 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据