Organic synthesis; Dental adhesives; Acrylamides; Differential Scanning Calorimetry; Cytotoxicity; Degree of conversion
资金
- CAPES (Coordenacao de Aperfeicoamento de Pessoal de Nivel Superior)
Objective. Synthesize and characterize a methacrylamide monomer for adhesive system and evaluate the physicochemical properties of the adhesive resin. Methods. The liquid methacrylamide monomer N,N',N ''-(nitrilotris(ethane-2,1-dyil)tris(2-methylacrylamide) (TMA) was prepared by reaction of methacrylic anhydride and tris(2-aminoethyl)amine with 60% yields. The TMA structure was analyzed by H-1 NMR, C-13 NMR, ATR-FTIR and UHPLC-QTOF-MS. Experimental adhesive resin containing bisphenol-A glycidyl methacrylate (BISGMA), 2-hydroxyethylacrylamide (HEAA), 2-hydroxyethylmethacrylate (HEMA) and TMA were formulated. Polymerization kinetics of neat TMA and experimental adhesive resin (TMA33%/HEAA66%, TMA50%/HEAA50%, TMA66%/HEAA33%, TMA50%/HEMA50%, BisGMA/HEAA/TMA and BisGMA/HEMA) were evaluated using Differential Scanning Calorimetry. Physiochemical properties for BisGMA/HEAA/TMA and BisGMA/HEMA adhesives were evaluated by cytotoxicity, ultimate tensile strength (UTS), softening in solvent (Delta KHN), contact angle (theta), microtensile bond strength (mu TBS) and failure analysis. A primer was also formulated with H2O/HEAA/AMPS (2-acrylamido-2-methylpropane sulfonic acid) and the pH value was verified and compared to commercial primer. Results. Adhesive resin with only HEAA and TMA (TMA33%/HEAA66%, TMA50%/HEAA50%, TMA66%/HEAA33%) showed lower conversion and polymerization rate after 40 s of light activation. Conversion up to 60% was found for BisGMA/HEAA/TMA and BisGMA/HEMA adhesive resin without significant difference between groups, p > 0.05. Cytotoxicity, UTS, mu TBS, Delta KHN and theta showed no statistical difference, p > 0.05, between BisGMA/HEAA/TMA and BisGMA/HEMA adhesive resin. Significance. In this study, the proposed synthetic route resulted in a tris(methacrylamide). A new primer composed without acrylates or methacrylates was formulated for 3-step etch-and-rinse adhesive system without the presence of HEMA monomer. Physicochemical properties and cell viability of BisGMA/HEAA/TMA adhesive resin represents an alternative adhesive resin without HEMA monomer. (C) 2018 The Academy of Dental Materials. Published by Elsevier Inc. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据