DENTAL MATERIALS
卷 26, 期 6, 页码 545-552出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.dental.2010.02.002
关键词
Zirconia; Y-TZP; Interface; All-ceramic; X-ray diffraction; Veneering material
Objectives. The metastability of the tetragonal crystal structure of yttria partial stabilized zirconia polycrystalline (Y-TZP) ceramics is a basis of concern for dental restorations. Reactions between the porcelain and the Y-TZP framework may result in a reduction of the stability of the zirconia and interface bonding caused by a transformation from tetragonal to monoclinic crystalline structure during veneering. Methods. XRD2 micro-diffraction measurements were carried out on tapered veneered cross-sections of the interface area to generate locally resolved information of the phase content in this region. To get a high intensity X-ray beam for short measurement times a focussing polycapillary with a spot size of app. 50 mu m was used to evaluate the porcelain zirconia interface. Results. Under almost all conditions the phase composition of zirconia grains at the interface revealed both the monoclinic and tetragonal structure. These observations indicate that destabilization of the tetragonal phase of zirconia occurs at the interface during veneering with porcelain. Significance. These results and their relevance to the long-term stability of the interface adhesion between zirconia and veneering porcelain as well as the tetragonal to monoclinic crystal transformations at the interface are discussed. (C) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据