Thermomechanical process optimization of U-10wt% Mo - Part 2: The effect of homogenization on the mechanical properties and microstructure

In the first part of this series, it was determined that the as-cast U-10Mo had a dendritic microstructure with chemical inhomogeneity and underwent eutectoid transformation during hot compression testing. In the present (second) part of the work, the as-cast samples were heat treated at several temperatures and times to homogenize the Mo content. Like the previous as-cast material, the homogenized materials were then tested under compression between 500 and 800 degrees C. The as-cast samples and those treated at 800 degrees C for 24 h had grain sizes of 25-30 mu m, whereas those treated at 1000 degrees C for 16 h had grain sizes around 250 mu m before testing. Upon compression testing, it was determined that the heat treatment had effects on the mechanical properties and the precipitation of the lamellar phase at subeutectoid temperatures. (C) 2015 Elsevier B.V. All rights reserved.