Rhenium volatilization in waste glasses

We investigated volatilization of rhenium (Re), sulfur, cesium, and iodine during the course of conversion of high-level waste melter feed to glass and compared the results for Re volatilization with those in low-activity waste borosilicate glasses. Whereas Re did not volatilize from high-level waste feed heated at 5 K min(-1) until 1000 degrees C, it began to volatilize from low-activity waste borosilicate glass feeds at similar to 600 degrees C, a temperature similar to 200 degrees C below the onset temperature of evaporation from pure KReO4. Below 800 degrees C, perrhenate evaporation in low-activity waste melter feeds was enhanced by vigorous foaming and generation of gases from molten salts as they reacted with the glass-forming constituents. At high temperatures, when the glass-forming phase was consolidated, perrhenates were transported to the top surface of glass melt in bubbles, typically together with sulfates and halides. Based on the results of this study (to be considered preliminary at this stage), the high-level waste glass with less foaming and salts appears a promising medium for technetium immobilization. Published by Elsevier B.V.