卷 15, 期 48, 页码 10597-10603出版社
ROYAL SOC CHEMISTRY
DOI: 10.1039/c3ce41753k
关键词
-
资金
- National Natural Science Foundation of China [21173084]
- Large Instruments Open Foundation of East China Normal University
Prussian blue analogue K2Zn3[Fe(CN)(6)](2)center dot xH(2)O microplates were synthesized via a hydrothermal-assisted precipitation method in the mixed solvent of isopropanol and deionized water at 120 degrees C for 24 h. The as-synthesized products were identified as a pure phase by X-ray diffraction (XRD). Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) images showed that single-crystalline quasi square microplates with a fairly uniform morphology were successfully prepared. The average thickness and side length of the microplates were about 160 nm and 750 nm, respectively. The effects of the ratio of (CH3)(2)CHOH/H2O in the reaction system and the surfactant (polyvinyl pyrrolidone, PVP) on the morphology of the products were investigated. The experimental results showed that PVP and the solvent isopropanol played important roles in the formation of the uniform microplates. A magnetic nanoporous ZnFe2-xO4-ZnO composite could be obtained from K2Zn3[Fe(CN)(6)](2)center dot xH(2)O microplates after calcination at 500 degrees C. The composite showed a good photocatalytic property in the degradation of rhodamine B and could be easily separated from the reaction mixture through magnetic separation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据