The synthesis of lotus-root-like NiO nanosheets and flower-like NiO microspheres was realized through a simple hydrothermal method and subsequent calcination. The diameter of the lotus-root-like NiO nanosheets is about 400 nm and the pore size is about 5 similar to 20 nm. The diameter of the flower-like NiO microspheres is about 2.5 mu m, and are composed of staggered lotus-root-like nanosheets. During the synthetic procedure, aqueous ammonia was used as an alkaline complexing reagent, and PVP was used as the template. Interestingly, when the pH value of the precursor solution increased from 8.30 to 10.80, the NiO nanosheets gradually assembled into microspheres, indicating that aqueous ammonia plays a key role in controlling the final morphology. Based on the experimental observation and analysis, a possible mechanism is proposed to understand the formation of the NiO nanostructured materials. In addition, the resultant NiO nanostructures present anomalous magnetic properties and display a spin-glass state at low temperature.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据