期刊
CRYSTAL GROWTH & DESIGN
卷 12, 期 5, 页码 2495-2500出版社
AMER CHEMICAL SOC
DOI: 10.1021/cg3001174
关键词
-
资金
- National Research Foundation of Korea (NRF)
- Ministry of Education, Science and Technology [2010-0029714]
- Center for Inorganic Photovoltaic Materials [20120001170]
- Korea government (MEST)
- MICE/KEIT [KI1002182]
- Korea Institute of Energy Technology Evaluation and Planning (KETEP)
- MKE [2011-8520010050]
- NRF
- MEST [2011-0009494]
- National Research Foundation of Korea [2009-0094038, 2011-0009494] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
This paper reports the effects of substrate temperature on the microstructural characteristics and electrical properties of p-type semiconducting NiO thin films grown on (0001) Al2O3 substrates. NiO thin films were biepitaxially grown on (0001) Al2O3 substrates by radiofrequency magnetron sputtering, and they showed specific crystallographic orientation relationships: [(1) over bar(1) over bar0](NiO)parallel to[01 (1) over bar0](Al2O3), [(1) over bar1 (2) over bar](NiO)parallel to[2 (1) over bar(1) over bar0]Al2O3 (in-plane), and [(1) over bar 11](NiO)parallel to[000 (1) over bar](Al2O3) (out-of-plane). Thus, a low lattice mismatch of 7.52% was obtained between the NiO thin films and the (0001) Al2O3 substrates. The film grown at 600 degrees C consisted of cubic and rhombohedral NiO grains, while the NiO thin films grown at substrate temperature below 400 degrees C only consisted of cubic NiO grains. Atoms at the grain boundaries between the cubic and the rhombohedral NiO grains perfectly coincided with each other because of the same atomic stacking sequences along [11 (1) over bar](c-NiO) and [0003](r-NiO) and with equal interatomic distances. Further, the paper discussed the observations of the perfectly coinciding nickel and oxygen atoms at the grain boundaries between the cubic and the rhombohedral NiO grains using high-resolution transmission electron microscopy (HRTEM) along with atomic modeling on the atomic scale. In addition, the dependence of the electrical properties of the NiO thin films on the substrate temperature and crystallinity is presented in this paper.