Transmission electron microscopy (TEM) and scanning electron rnicroscopy (SEM) have been carried out to clarify the microstructure of Bi2Se3 thin films grown by molecular beam epitaxy (MBE) on Si(111) and InP(111) substrates. The film grown on InP displays much better overall quality at the microstructural level than does the film grown on the Si substrate. A layer of poor crystalline quality at the interface followed by well-crystallized Bi2Se3 has been observed for both substrates. The thickness of this interface layer is not uniform; it varies across the sample from zero, showing a sharp interface between the substrate and Bi2Se3, up similar to 1 to nm and similar to 1.8 nm for Bi2Se3/InP and Bi2Se3/Si, respectively. Formation of rotation twin domains and lamellar twins has been observed and is described in detail for both substrates.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据