CRYSTAL GROWTH & DESIGN
卷 9, 期 11, 页码 4814-4821出版社
AMER CHEMICAL SOC
DOI: 10.1021/cg900648q
关键词
-
资金
- Spanish Ministerio de Ciencia c Innovacion (MICINN) [MAT 2007-66309-C02-02]
- Generalitat de Catalunlya
Mesoporous NiCo2O4 spinel has been synthesized by nanocasting, using SBA-15 and KIT-6 silica its hard templates. Two temperatures of calcination were applied for the conversion of the spinel precursors (metal nitrates) into NiCo2O4. At 375 degrees C the pure spinel was obtained, whereas at 550 degrees C NiO impurities were detected. The mesoporous powders obtained were characterized by transmission electron microscopy, X-ray diffraction, Brunauer-Emmett-Teller analysis, and magnetic measurements. In addition. their thermal stability was assessed by post heat-treating the materials at 550 degrees C: the mesostructure of the pure spinel (calcined at 375 degrees C) collapsed, leading to the disruption of the porous network, while the mesoporosity of the powders calcined at 550 degrees C was preserved. In all cases, the post-thermal treatment induced the segregation of NiO; the final NiO amount was found to be in the 7-10 wt % range.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据