CRYOGENICS
卷 51, 期 1, 页码 55-61出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.cryogenics.2010.11.001
关键词
Metals; Structural material; Mechanical properties; Phase transitions; Tribology
This paper focuses on the effects of low temperature (subzero) treatments on microstructure and mechanical properties of H13 hot work tool steel. Cryogenic treatment at -72 degrees C and deep cryogenic treatment at -196 degrees C were applied and it was found that by applying the subzero treatments, the retained austenite was transformed to martensite. As the temperature was decreased more retained austenite was transformed to martensite and it also led to smaller and more uniform martensite laths distributed in the microstructure. The deep cryogenic treatment also resulted in precipitation of more uniform and very fine carbide particles. The microstructural modification resulted in a significant improvement on the mechanical properties of the H13 tool steel. (C) 2010 Elsevier Ltd. All rights reserved.