期刊
CORROSION SCIENCE
卷 55, 期 -, 页码 54-60出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2011.10.002
关键词
Steel; Polarization; SEM; Cathodic protection; Stress corrosion
资金
- National Natural Science Foundation of China [50901041]
- China Postdoctoral Science Foundation [20100480196]
- Canada Research Chairs Program
This paper investigates mechanistically stress corrosion cracking (SCC) of an X70 pipeline steel that is under cathodic protection (CP) in a near-neutral pH solution. It was found that there is a critical potential range, i.e., -730 and -920 mV(SCE), where the steel is in a non-equilibrium electrochemical state, and anodic dissolution (AD) reaction may occur when the steel is polarized cathodically. When the applied potential is more positive than this range, SCC is AD-based; while the applied potential is more negative. SCC of pipelines is under hydrogen embrittlement (HE) mechanism. When the polarization potential is within the range. SCC of the steel is under the combined effect of AD and HE. Therefore, AD may still occur on pipeline steel that is under CP with the potential within this critical range, contributing to the cracking process. (C) 2011 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据