CORROSION SCIENCE
卷 53, 期 4, 页码 1214-1223出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2010.12.006
关键词
Aluminium; Alloy; Intermetallics; AES; Pitting corrosion
This study investigates the formation of a chromate conversion coating at Al-Cu-Fe-Mn intermetallic sites of an Al2219 alloy and the corrosion initiation at these sites in a 3.5% NaCl solution, using SEM, AES and EDX. Changes in the surface chemistry were monitored after progressive exposures to the solution up to 42 h. The coating was found to be thinner and more defective on the intermetallic. Initially, Al is dissolved and Al(OH)(3) deposited on and around the intermetallic. After 42 h of exposure, Al(OH)(3), Fe and Mn oxides and small particles of elemental Cu are deposited as corrosion products. (C) 2010 Elsevier Ltd. All rights reserved.