Corrosion of Mg-Y alloys was studied using electrochemical evaluations, immersion tests and direct observations. There were two important effects. in 0.1 M NaCl, the corrosion rate increased with increasing Y content due to increasing amounts of the Y-containing intermetallic. In 0.1 M Na2SO4, the corrosion rate decreased with increasing Y content above 3%, attributed to a more protective surface film, despite the intermetallic. The corrosion rate evaluated by electrochemical impedance spectroscopy was somewhat smaller than that evaluated from H evolution as expected from the Mg corrosion mechanism. A mechanism is proposed for filiform corrosion. Direct in situ corrosion observations revealed that a predominant feature was hydrogen evolution from particular parts of the alloy surface. (C) 2010 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据