期刊
CORROSION SCIENCE
卷 51, 期 5, 页码 1115-1127出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2009.02.017
关键词
Magnesium; Intermetallics; XPS; Surface films; Dealloying
资金
- Australian Research Council
- Centre of Excellence
- Design of Light Alloys in Australia
- CNRS in France
- Furthermore
- Complex Metallic Alloy (CMA) Network of Excellenc
- European Research Commission [NMP3-CT-2005-500140]
An XPS investigation was carried out of the surface films, formed by exposure to ultrapure water, on mechanically ground Mg and the two Mg-Al intermetallic compounds: Al3Mg2 and Mg17Al12. The mechanically ground Mg surface had a film of MgO at the Mg metal surface covered by a Mg(OH)2 layer. formed by the reaction of the MgO with water vapour in the air. Upon immersion in ultrapure water, this film converted to a duplex film with an inner MgO layer next to the Mg metal and an external porous hydroxide layer. For both intermetallics, the XPS data is consistent with (i) preferential dissolution of Mg and (ii) a 10 nm thick film on the surface after immersion in ultrapure water; the film composition on Al3Mg2 was AlMg1.4O0.2(OH)(5.4) whilst on Mg17Al12 the composition was AlMg2.5(OH)(8). (C) 2009 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据