The effect of Si additions on the high temperature oxidation of a ternary Ni-10Cr-4Al alloy in 1 atm O2 at 1100 °C

The oxidation of four Ni-10Cr-ySi-4Al alloys was studied at 1100 degrees C to examine the effects of Si additions (from 2 to 6 at.%) on the behavior of the alloy Ni-10Cr-4Al. Addition of 2 at.% Si prevented completely nickel oxidation, but could not form alumina scales. Larger Si additions produced alumina only over part of the alloy surface (about 20% with 4 at.% Si and 30% with 6 at.% Si), but could not prevent completely the internal oxidation of Al. The results are interpreted by extending to quaternary alloys the mechanism of the third-element effect already proposed for ternary alloys. (C) 2008 Elsevier Ltd. All rights reserved.